Effects of TiO2 Particles Size and Heat Treatment on Friction Coefficient and Corrosion Performance of Electroless Ni-P/TiO2 Composite Coatings

Elina Esmaeel Nad, Maryam Ehteshamzadeh

Abstract

УДК 621.7

 

The effects of the titanium dioxide (TiO2) particles size on the friction coefficient and corrosion performance of the Ni-P/TiO2 composite coatings before and after heat treatment at 400oC for 1h have been investigated. Pin-on-disc analysis results have revealed that the highest and the lowest friction coefficients belonged, respectively, to the simple Ni-P coating and the Ni-P/TiO2 composite coating containing TiO2 particles of the average size of 0.1 μm (μ ~ 0.62 against 0.52). Eventually, a relative reduction in the corrosion resistance and the friction coefficient (as low as μ ~ 0.38) have been observed after heat treatment of Ni-P and Ni-P/TiO2 composite coatings. 

 

Keywords: particle-reinforcement, friction, corrosion, EIS.

 

 

В работе рассматривается влияние размера частиц двуокиси титана (TiO2) на коэффициент трения и характеристики коррозии покрытий из сложного сплава Ni-P/TiO2 до и после тепловой обработки при 400oC в течение 60 мин. Анализ на трение и износ по схеме «штифт-диск» показал, что наибольший и наименьший коэффициенты трения наблюдались при простом Ni-P покрытии и при сложном Ni-P/TiO2, с частицами TiO2 со средним размером 0,1 μm (μ ~ 0,62 в отличие от 0,52). В действительности, относительное уменьшение сопротивления коррозии и коэффициента трения (до μ ~ 0,38) наблюдалось после тепловой обработки покрытий как из Ni-P, так и из Ni-P/TiO2.

 

Ключевые слова: укрупнение частиц, трение, коррозия, спектроскопия электрохимического импеданса.

 

 