Vol. 45 (2009), Issue 3, p. 70-77

ELECTRICAL PROCESSES IN ENGINEERING AND CHEMISTRY

Evolution of PZC with Thermal Transformation of Tunisian Kaolinite

Chelly M., Kriaa A., Hamdi N., Srasra E.

Abstract

УДК 541.183

 

The purpose of this paper is to study the thermal behaviour of Na+-saturated Tunisian kaolinite (ka-Tab) with the evolution of its point of zero charge (PZC). The Fourier Transform Infrared spectroscopy (FTIR), X-Ray Diffraction (XRD), Differential Thermal Analysis (DTA), Cation Exchange Capacity (CEC) and specific surface area (SSA) were used to characterize the kaolinite sample.  In the present investigation, the focus was on the surface charge characteristics of kaolinite at different temperature of heating. The results show that the formation of new phases in the kaolinite structure at temperature > 500-600°C, shifts the PZC value towards 8 which approximately PZC value of γ-Al2O3.

 

Методами физико-химического анализа (FTIR, XRD, DTA, ионного обмена и ВЕТ) изучено поведение тунисского каолинита при термическом прокаливании при температурах 100-10000С. Показано, что при температуре выше 600 0С в каолините образуются новые фазы, обусловливающие сдвиг pH точки нулевого заряда (ТНЗ) к значениям ТНЗ g-Al2O3. Приводятся спектры-ИК, РФА, а также адсорбционные и ионообменные характеристики термообработанного каолинита.

Download full-text PDF. 1490 downloads

Web-Design Web-Development SEO - eJoom Software. All rights reserved.