Effect of Gamma Radiation on Oxidation of Electroless Ni-P Deposited on Stainless Steel st. 304

Hashemi M.Y., Garibov A.A., Agayev T.N.

Abstract

УДК 544.54:621.039.531

 

 

The given work deals with the effect of γ-irradiation on the oxidation process of the Ni-P chemical deposition on the surface of the stainless steel marked 304. The methods used are scanning electron microscopy and X-ray analysis. As a result, it has been found out that after γ-irradiation the surface of the Ni-P layer is completely covered with cracks, and on the surface of this layer a high content of oxygen and phosphor has been detected because of formation of the P2O5 oxide.

 

Keywords: Ni-P layer, surface morphology, gamma-radiation, structure.

 

 

В настоящей работе исследовано влияние γ-излучения на процесс окисления Ni-P химически осажденного покрытия на нержавеющей стали марки 304 методом сканирующей электронной микроскопии (SEM) и рентгеновского анализа (EDX). Установлено, что после γ-излучения поверхность Ni-P слоя былa полностью покрыта трещинами, и на поверхности Ni-P слоя обнаружено высокое содержание кислорода и фосфора из-за образования оксида Р2О5.

 

Ключевые слова: слой Ni-P, морфология поверхности, гамма-облучение, структура. 

 

 